Polystyrene foam sheet manufacture

ABSTRACT

The method of making polystyrene foam for foam products which includes utilizing atmospheric gases as the blowing agents or preferably mixing one or more of these gases and a blending agent which is non-volatile at the extrusion temperatures, introducing the mixture to a molten thermoplastic polystyrene resin containing nucleating agents such as sodium bicarbonate and citric acid and extruding the thermoplastic in the form of a foam. The resultant foam has substantially no residual blowing agent, is dimensionally stable at ambient temperatures and when used with a non-volatile blending agent can be made with small amounts of blowing agent permitting cooling of the melt without high loading on the extruder. The foam may be coextruded with one or more layers of thermoplastic film so that the resultant product is adapted for use for plates, cups, food containers or packaging and for labels for containers such as glass and plastic containers and for labels that are shrunk in place on a container.

This is a continuation of copending application Ser. No. 07/752,430 filed on Aug. 30, 1991 which is a continuation of application Ser. No. 07/538,291 filed Jun. 14, 1990, now U.S. Pat. No. 5,082,608, now abandoned.

This invention relates to manufacture of foam and particularly the manufacture of polystyrene foam.

BACKGROUND AND SUMMARY OF THE INVENTION

In the manufacture of polystyrene foam, it has been common to utilize blowing agents such as chlorofluorocarbons solely or together with alkanes, usually pentdue or isopentane. Such a foam is usually made by extrusion. Due to the solubility of chlorofluorocarbons and certain alkanes in polystyrene, the extrusion melt viscosity is reduced and this permits sufficient cooling of the melt so that high load, indicated by amperage, will not be applied to the extruder drive motor.

Pentdue and chlorofluorocarbons such as Freon 11 and 12, for example, are partially soluble in polystyrene and reduce the melt viscosity enabling the extruder adequately to cool and extrude the molten plastic material at lower loads and temperatures in order to generate a good smooth foam surface and appearance, small cell size control for opacity and other foam physical properties such as orientation, shrinkage characteristics and stiffness. Loss of residual blowing agent over a period of time, however, creates a shrinkage in the sheet material, an increase in thickness and an increase in softening point temperature as the residual blowing agent is reduced.

Where the foam is intended for use as a label on glass or plastic containers wherein the label is shrunk in place, the foam material is extruded and stretched in one direction more than the other. Preferably, the label material is coextruded with a plastic film. The gradual loss of residual blowing agent causes the label material to vary in shrinkage characteristics.

U.S. Pat. No. 4,424,287 is directed to a polymer foam process for making thermoformed articles wherein the blowing agent comprises at least an atmospheric gas and at least one volatile plasticizing blowing agent. As stated in this patent, early attempts to mix normally liquid hydrocarbons and normally gaseous blowing agents have not been successful and it is necessary that great care be exercised in production of a polymer foam with highly-volatile blowing agents such as carbon dioxide even in such a mixture. Accordingly, as set forth in this patent, it was thought necessary to utilize both the inert gas such as carbon dioxide and a volatile plasticizing organic blowing agent such as pentane and to thermoform the articles immediately after extrusion.

U.S. Pat. No. 4,436,679 discloses a method of making foam wherein water and natural gas are introduced into a melt.

U.S. Pat. No. 4,470,938 discloses a method of utilizing atmospheric gases for forming thermoformed articles wherein the process includes introducing, to a molten resin charge under pressure, a gas blowing agent from a supply gas source of comparatively higher pressure, said introducing being by means of discrete uniform volumetric charges of gas into said resin, wherein said discrete volumetric charges are introduced by means of a free piston-cylinder combination given motive power by said supply gas source. Although this patent mentions the use of a number of atmospheric gases, no claim was made as to any beneficial results as to the product and no commercial use has been made of such a process.

Among the objectives of the present invention are to provide a method of making polystyrene foam wherein the method utilizes atmospheric gases as blowing agents which are inherent in the atmosphere; wherein the blowing agent is substantially entirely released when the polystyrene foam is extruded; wherein the melt can be cooled to normal process levels and not create high loading on the extruder or shear heat from high polymer viscosity; wherein the amount of shrinkage can be controlled as may be required for the ultimate use of the foam; wherein the density and cell size can be controlled; and which utilizes conventional extrusion apparatus.

In accordance with the invention, the method of making polystyrene foam comprises mixing an atmospheric gas such as carbon dioxide, nitrogen or air and preferably a non-volatile blending agent, introducing the gas or the mixture to a molten thermoplastic polystyrene resin containing nucleating agents such as sodium bicarbonate and citric acid and extruding the thermoplastic in the form of a foam. The resultant foam has substantially no residual blowing agent, is dimensionally stable at ambient temperatures and when used with a non-volatile blending agent can be made with small amounts of blowing agent permitting melt cooling without high loading on the extruder. The foam may be coextruded with one or more layers of a thermoplastic film so that the resultant product is adapted for use for plates, cups, food Containers or packaging and for labels for containers such as glass and plastic containers and for labels that are shrunk in place on the container.

DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic drawing of an extrusion apparatus utilized in the method.

FIG. 2 is a partly schematic diagram of a portion of the extrusion apparatus.

FIG. 3 is a schematic drawing of an apparatus utilized in the process downstream of the extruder.

FIG. 4 is a partly schematic diagram of a modified form of extrusion apparatus.

DESCRIPTION

In accordance with the invention, an atmospheric gas such as carbon dioxide, nitrogen or air alone or preferably combined with a blending agent which is non-volatile at the extrusion temperatures such as a high molecular weight ester having low volatility at high temperatures is introduced into the thermoplastic molten polystyrene melt, and the mixture is extruded.

Where a mixture of atmospheric gas and a blending agent which is non-volatile at the extrusion temperatures is used, the atmospheric gas and the non-volatile blending agent may be mixed prior to introduction or separately.

Referring to FIG. 1, the atmospheric gas is supplied to the first stage of a tandem extruder system through a pressure regulator, heater, two stage gas booster and accumulator, mass flow meter control valve, second heater and pressure regulator to the molten massive plastic material in the first or primary extruder section. Where the liquid non-volatile blending agent such as the non-volatile ester is used, it is pumped to an accumulator and thereafter to a mass flow meter and-control valve for injection into the plastic material downstream of the point of injection of the atmospheric gas. Alternatively, the blending agent can be mixed with the atmospheric gas in a static mixer and injected at a single point of injection. The blended material then passes to the secondary conditioning or cooling extruder and is extruded in the form of a tubular web that is preferably cooled from the inside and outside.

Referring to FIG. 2, in a preferred form of the invention, the internal cooling mandrel M onto which the tubular material is passed is located relative to the extruder die D such that the frustoconical web W forms an angle A with the axis of the extruder that is preferably greater than 45° and ranges between 45° and 90°. In addition, the cooling air is supplied to the exterior of the tubular web closely adjacent the extruder die lip and is caused to flow parallel to the web W. Specifically, the air is supplied at an acute angle B tangentially of the web W as it is expanded outwardly to cool the external surface of the web W. This flow of air causes additional ambient air to be drawn to supplement the air being supplied for maximum cooling by turbulent flow. Cooling of the web and moving the web at an angle greater than 45° minimize and substantially eliminate axially extending corrugations which occur in making foam materials with atmospheric gases.

In the form of the invention shown in FIG. 4, in addition to the arrangement in FIG. 2, there is provided a tapered cooling ring R adjacent the front of the cooling mandrel. The ring R is cooled by lines L and includes annular recesses R₁ and R₂ that are connected by a line P to a vent valve V to the atmosphere. As the web W contacts and passes over the tapered cooling ring R, which is maintained at a temperature independent of that of the mandrel M, further cooling of the web occurs at a smaller diameter than that of the mandrel. As the web cools, a force is required to pull and stretch the web over the tapered cooling ring creating a tension between the mandrel M and the conventionally used pull rollers. The provision of the annular recesses R₁, R₂ being vented through a vent port produces a partial vacuum as the web moves across in contact with the cooling ring R maintaining the web in good contact with the cooling ring R. By use of the valve, the degree of venting can be increased or decreased such that the degree of vacuum can be increased or decreased.

It has been found that utilizing a percentage of atmospheric gas by weight of less than 3% by weight produces satisfactory results.

It has been found that when a non-volatile blending agent such as an ester is also used, the method permits the ready processing of the polystyrene melt by cooling without high loading on the extruder and so that the blowing agent is substantially entirely released upon extrusion of the foam. The resultant product has controlled rate of shrinkage without change in aging, cell size, opacity, stiffness, smoothness, caliper, density, low cost, but most important environmentally acceptable.

As used herein, the non-volatile blending agent comprises a high molecular weight agent which is non-volatile at the extrusion temperatures such as 300°-325° F. The molecular weight of the non-volatile blending agent preferably ranges between 350 and 450. Non-volatile blending agents which have produced satisfactory results comprise diisodecyl adipate, ditridecyl adipate and trioctyl trimellitate.

The aforementioned non-volatile blending agents can be used alone or in blends or mixtures for control and adjustment of viscosity.

The thermoplastic material must include a nucleating agent such as sodium bicarbonate and citric acid, as is well known in the art.

For use in extruding a polystyrene foam sheet which has functional properties suitable for use in application by shrinkage from a formed sleeve to conform to the contour shape of a container to perform as a label, the method comprises utilizing other atmospheric gases such as carbon dioxide, nitrogen or air as the sole and exclusive blowing agent for producing said foam sheet. The method preferably incorporates the injection of the high molecular weight non-volatile blending agent having very low volatility at extrudate temperatures (e.g., 300° F.-325° F.) into the polymer melt. Such material provides a solvating action weakening intermolecular bonding of the polymer and reducing melt viscosity. Preferably, directly downstream following the injection of the organic fluid, air (carbon dioxide, nitrogen or air, or blends thereof) after having been compressed in excess of extruder injection point pressure (typically, in excess of 3000 PSI), is injected through a second injection port into the polymer.

As indicated in FIG. 1, the extrusion equipment used may be a conventional tandem system employing two extruders working in conjunction with each other whereby the first extruder melts the polymer mixed with nucleating agent, which accepts by injection and mixes in a blowing agent and transfers said mix to a second extruder which cools the melt and conveys it into an annular die which transforms the melted mass into a continuous sheet foam.

No extrusion equipment modifications such as screw designs, die designs, or special mixing devices are necessary. Standard type pumps as suitable for organic fluids and as suitable for boostering industrial type gas pressure with appropriate metering devices which are known to those skilled in the art are the only equipment changes by addition or modification.

In the past, CFCs (chlorofluorocarbons) or HCFCs (hydrochlorofluorocarbons) and alkanes (usually pentane or isopentane) were commonly used as blowing agents in the industry to produce polystyrene foam sheet which is converted into a variety of products such as disposable cups, meat trays, egg cartons, etc. Such fluorocarbons and alkanes are partially soluble in polystyrene hence reducing the melt viscosity and permitting process cooling of the extruder melt without creation of high load or power demand on the extruder drive motor.

The use of blowing agents such as atmospheric type inert gases (carbon dioxide, nitrogen, air) create two significant differences compared to CFCs, HFCs or alkanes:

(I) The amount (usage) of blowing agent is greatly reduced. For example, the following table illustrates approximate comparative amounts of blowing agent needed to produce a label type foam in the caliper range of 5-12 mils having a density area around 12-20 PCF:

                  TABLE 1                                                          ______________________________________                                         Blowing Agent    Usage %                                                       ______________________________________                                         Freon 11         5-7                                                           Freon 12         3-5                                                           Pentane/Isopentane                                                                              3-5                                                           Freon 22         1-3                                                           Carbon dioxide   1-2                                                           Air              .5-1                                                          Nitrogen         .5-1                                                          ______________________________________                                    

It can be seen that carbon dioxide is effective in a much lower amount than prior blowing agents for comparable densities. With nitrogen and air, even lesser amounts are needed.

(2) Inasmuch as the atmospheric gases are relatively insoluble in the polystyrene, the resultant foam material can be stored and used at various times without any substantial change in the properties thereof including the shrinkage properties.

This may be contrasted to fluorocarbons and alkanes which are soluble in polystyrene and reduce the melt viscosity enabling the extruder to convey or advance the material at lower power loads with considerable latitude to cool the melt to around 300° F. before exiting from the die as necessary to generate good smooth foam without ruptured cells and obtain other foam sheet physical properties such shrinkage characteristics and stiffness. Due to the solubility of the CFCs and alkanes approximately half or greater of the amount of these type materials injected remains dissolved in the polystyrene after emerging from the die. These materials are volatile and will gradually evaporate from the sheet with age over a period of months. Label stock intended for application onto a container or bottle by use of shrinkage obviously requires that shrinkage properties be a part of the sheet characteristics. The CFCs and alkanes act as plasticizers in polystyrene lowering the Tg of the polymer and enhancing shrinkage upon application of sufficient heat. The amount of shrinkage and the temperature at which shrinkage will start is dependent upon how much residual CFC or alkane is present in the sheet.

The following data illustrates the effect of temperature on shrinkage of a sheet containing 2% residual fluorocarbon. Sample used was 7 mil caliper with 20 PCF density:

                  TABLE 2                                                          ______________________________________                                         Temperature % Machine Direction Shrinkage                                      ______________________________________                                         200° F.                                                                              6.0                                                               210° F.                                                                             14.0                                                               220° F.                                                                             45.0                                                               230° F.                                                                             55.0                                                               240° F.                                                                             60.0                                                               250° F.                                                                             62.0                                                               ______________________________________                                    

However, as stated fluorocarbon are volatile at room temperature and the amount of fluorocarbon will gradually decrease with age. Rate of loss is obviously dependent upon storage conditions, whether in roll form, width of web, etc. In an accelerated lab test with a sample sheet, exposed for test purposes the shrinkage rate of loss is illustrated as follows using 210° F. to simplify data:

                  TABLE 3                                                          ______________________________________                                                       % Machine Direction Shrinkage                                    Aging Period (weeks)                                                                         @ 210° F.                                                 ______________________________________                                         0             14.0                                                             1             10.0                                                             2             9.0                                                              3             8.0                                                              4             7.0                                                              5             6.0                                                              ______________________________________                                    

In a process where foam labels are applied by shrinkage onto a container or bottle, high applicating speeds such as 500-1000 units/minute are used. This places significant importance on the shrinkage rate and on-set of shrinkage temperature in order to obtain a smooth conformance of the foam to the contour of the container shape without wrinkling. Use of a volatile blowing agent presents a variable in shrinkage properties so that consistent label application may not be achieved in order to obtain a smooth conformance with the container. Also, in some cases the increased need for heat to shrink leads to a blistering effect on the printed label surface diminishing the aesthetic appearance of the label.

The present method utilizes atmospheric gases (including air, nitrogen, carbon dioxide or mixtures thereof) and preferably contemplates injecting into the melt a non-volatile blending agent such as a high molecular weight ester having excellent stability to heat whereby it is resistant to decomposition with heat and within practical purposes can be considered as nonvolatile in the application process of polystyrene foam extrusion. While the number of non-volatile blending agents meeting such criteria is limited, ditridecyl adipate and trioctyl trimellitate or blends thereof for viscosity adjustment have successfully been utilized, diisodecyl adipate being considered marginally acceptable for inclusion to the list due to a slightly higher tendency to volatilize with heat exposure.

Organic materials were evaluated in the laboratory by exposing them to conditions more extreme than encountered in extrusion. Each material was placed in a wide mouth open cup and held at a temperature of 155° C. with measurement of volatile loss at different time intervals. Data on the three liquid blending agents above were as follows:

                  TABLE 4                                                          ______________________________________                                                    Molecular                                                                               % Volatility @ 155° C.                              Name         Weight     After 2 hours                                                                            24 hours                                     ______________________________________                                         Diisodecyl Adipate                                                                          427        0.3       6.0                                          Ditridecyl Adipate                                                                          510        0.2       2.8                                          Trioctyl Trimellitate                                                                       550        0.6       1.5                                          ______________________________________                                    

Examples of materials which did not meet the acceptable criteria for use are illustrated as follows:

                  TABLE 5                                                          ______________________________________                                                    Molecular                                                                               % Volatility @ 155° C.                              Name         Weight     After 2 hours                                                                            24 hours                                     ______________________________________                                         Diisooctyl Adipate                                                                          373        1.7       24.1                                         Dibutyl Sebacate                                                                            316        4.3       60.4                                         Diisobutyl Azelate                                                                          303        14.0      97.0                                         Triethylene  430        2.1       27.5                                         Glycolcaprate-                                                                 caprylate                                                                      ______________________________________                                    

The embodiment of the invention wherein the method includes injecting a non-volatile blending agent having highly selective heat resistance to decomposition and volatility while using an atmospheric type gas for the blowing agent can include a valving arrangement whereby the two materials are premixed and injected in the same port or the materials are injected into separate ports if the extruder is so equipped with two individual ports. No special mixing devices are necessary and no extruder screw modifications are needed. As known by those familiar with the art, a pump adequate for handling the liquid non-volatile blending agent and a pump for pumping atmospheric gas capable of building the pressure to the area of 3000-4000 PSI to permit injection into the extruder is necessary. Accordingly, a metering system appropriate for use with each material is required to control the usage rate.

The method of the present invention is especially advantageous for making foam material to be used in fabricating structures where a foam sheet must be shrunk. Labels as well as disposable cups are well known examples of such applications. Sheet material for both of these type applications have been produced within the embodiment of this invention with corresponding conversion to end use products. In label stock with a caliper use range of 5-12 mils and density area of 18-22 PCF, a usage rate of non-volatile blending agent of approximately 1.0% of the foam weight has been preferred. For cup stock in the caliper range of 16-22 mils and density area of 12-14 PCF, a usage rate of 2.0% of the foam weight has been successful.

To evaluate the benefit of the non-volatile blending agent, the following data was determined from tests on motor load measured by amperage and melt temperature at entry into the die. Ditridecyl adipate was used as the non-volatile blending agent:

                  TABLE 6                                                          ______________________________________                                                    Amount       Cooling  Melt Temp.                                    Blowing Agent                                                                             Blending Agent                                                                              Amperage of                                            ______________________________________                                         Nitrogen   0            119      318                                           Nitrogen   1.5           93      318                                           Carbon dioxide                                                                            0            105      329                                           Carbon dioxide                                                                            1.5           95      322                                           ______________________________________                                    

As can be seen, the addition of the blending agent functions to reduce the amperage required to maintain the same or lower melt temperature.

Another advantage of use of the non-volatile blending agent is that it will lower the Tg of the polymer and hence enhance onset of shrinkage at lower temperatures of the foam upon application of heat as previously indicated as needed in certain industrial applications. The relative effect of the concentration of the use of blending agent is indicated by the following data:

                  TABLE 7                                                          ______________________________________                                         Machine direction percent shrinkage * where                                    the organic fluid is diisodecyl adipate.                                       % Blending Agent                                                                            @ 200° F.                                                                          @ 210° F.                                                                        @ 220° F.                              ______________________________________                                         0            3.4         5.0     23.0                                          0.5          3.9         7.8     32.0                                          1.0          4.9        15.0     41.0                                          1.5          6.6        16.5     48.5                                          2.0          11.5       18.1     53.0                                          ______________________________________                                          * Melt temperature, web cooling conditions, molecular weight of the            polystyrene and output as examples can influence shrinkage and level of        shrinkage as such must be in concert with other properties required.     

Another advantage of the non-volatile blending agent is that shrinkage properties of the sheet are stabilized and do not deteriorate as rapidly with age as occurs where CFCs and alkanes are used as blowing agents which volatilize and leave the sheet with age. Shrinkage tests conducted on sheet immediately following extrusion and after a three-month aging period yield data typically indicated as follows:

                  TABLE 8                                                          ______________________________________                                                          % Shrinkage @ 220° F.                                  Blowing Agent                                                                            Blending Agent                                                                              At extrusion                                                                             After 3 months                                ______________________________________                                         Freon 11  None         12-14     4-6                                           Atmospheric gas                                                                          1.0%         12-14     10-12                                         ______________________________________                                    

Another advantage of the addition of a non-volatile blending agent of the type selected in combination with use of an atmospheric gas is that the blending agent does not evaporate and condense on the die lips, cooling air devices or sizing mandrel parts which may occur with volatile constituents present in the polymer melt. If CFCs and alkanes are used, dimers and oligomers from the polystyrene resin are soluble in CFCs and alkanes and will volatilize with these blowing agents upon exiting from the extrusion die. The dimers and oligomers will then tend to condense on cool metallic surfaces in the die mandrel area and accumulate to a point where liquid drips onto the web. These low molecular weight constituents will form blemishes on the sheet surface and weaken the sheet. In subsequent printing, blanking and/or slitting of such rolls at high speeds, these areas may create random tear outs usually leading to web breaks during processing.

A further advantage of the use of the atmospheric gases in making foam material in accordance with the invention is that the resultant foam sheet is less susceptible to gauge bands than foam made with plasticizing blowing agents such as CFCs and alkanes. This may be contrasted to foam made by utilizing the CFCs and alkanes where such gauge bands representing variations in thickness across the width of a sheet cut from an extruded tube which result in differences in caliper (gauge) called gauge bands. Since atmospheric gases are not soluble and are not present in the foam as would be the case when using CFCs and alkanes, the formed foam sheet is more resistant to stretching and compression thus allowing application of more tension and pressure in roll formation. FIG. 3 illustrates a modification in winder design to apply added pressure between the face of a reel drum surface winder and the forming roll. This modification allows direct continuous pressure on the range of 60-80 PSP as opposed to 20-50 PSI pressure transmitted through leverage linkage by a power cylinder C in the normal winding of foam where the pressure diminishes as the roll increases in diameter. This modification has been found to virtually eliminate gauge bands as long as typical gauge uniformity is maintained in the cross direction of the web. Gauge bands have been problematical in the foam industry for years creating distortions in the web in roll storage to later cause problems in printing, blanking, slitting or product performance. Much effort has therefore been used in the industry to make rotating dies and/or air rings or more sophisticated means to improve cross direction gauge uniformity. The use of atmospheric gases insoluble in the formed polystyrene foam sheet generates a less permanently deformable substrate thereby allowing added pressure to be applied in roll formation leading to a dramatic improvement in roll quality by the virtual elimination of gauge bands.

The following table represents examples of foam materials made by utilizing various atmospheric gases and the attained caliper and density with and without blending agents or varying the amount of blending agent.

                                      TABLE 9                                      __________________________________________________________________________     BLOWING % BLENDING                                                                            CALIPER                                                                             DENSITY                                                                             COOLING EXTRUDER                                                                           MELT                                                                               NON-FOAM LAYER                        AGENT % AGENT  MILS PCF  AVG °F.                                                                      AMPS                                                                               RPM                                                                               TEMP                                                                               CALIPER (MILS)                                                                           COMMENTS                    __________________________________________________________________________     Nitrogen                                                                             0.4                                                                              1.5    6.7  20.3 242  93  10.0                                                                              318 0.5                                         0.4                                                                              0      6.7  19.2 242  93  10.4                                                                              337 0.5       Melt 19°                                                                higher                            0.9                                                                              1.5    6.7  15.3 242  73  8.6                                                                               324 0.5       Shear heat with lower                                                          amps                              0.9                                                                              0      6.7  15.6 242  88  9.8                                                                               334 0.5                                         0.9                                                                              0      6.7  15.3 207  119 10.6                                                                              320 0.5       Gas dispersion poor                                                            chevrons & high amps              0.5                                                                              1.9    16.0 14.0 223  90  11.7                                                                              321 0.5                                   94% N.sub.2                                                                          0.4                                                                              1.5    6.7  20.1 244  92  10.1                                                                              320 0.5                                         0.4                                                                              1.5    6.7  17.7 244  92  10.1                                                                              310 0                                     Air   0.4                                                                              1.5    6.7  20.3 244  93  10.2                                                                              312 0.5                                         0.3                                                                              1.4    6.7  17.8 244  93  10.2                                                                              312 0                                           0.3                                                                              1.4    30.0 12.4 244  93  10.2                                                                              312 0                                     Helium                                                                               0.3                                                                              1.4    7.0  21.6 244  95  10.5                                                                              318 0.5                                   CO.sub.2                                                                             0.8                                                                              1.5    6.7  20.6 242  95  10.8                                                                              322 0.5                                         0.8                                                                              1.5    6.7  20.1 233  98  10.4                                                                              318 0                                           0.8                                                                              0      6.7  21.0 242  105 11.2                                                                              329 0.5       Amperage & melt temp                                                           increase                          1.0                                                                              0      6.7  18.4 242  102 11.1                                                                              326 0.5       Added Co.sub.2 lowers                                                          amps & melt temp                  1.0                                                                              0      6.7  18.4 228  110 11.6                                                                              322 0.5       At equal melt temp                                                             fluid                                                                          lowers amps                       1.0                                                                              0.8    6.7  18.0 242  95  10.9                                                                              322 0.5                                         1.0                                                                              1.5    6.7  18.0 242  90  10.1                                                                              319 0.5       Added fluid lowers                                                             amps & melt                       0.5                                                                              1.9    16.0 15.6 220  92  14.8                                                                              322 0.5                                         0.6                                                                              1.9    10.0 13.4 216  95  15.1                                                                              324 0.5                                         0.5                                                                              1.8    27.0 14.0 214  94  14.8                                                                              320 0                                     __________________________________________________________________________

Effects of increases in carbon dioxide usage on caliper and density and changes in line speed.

                  TABLE 10                                                         ______________________________________                                         Blowing   % Blending                                                                               Caliper   Density                                                                              Line Speed                                 Agent %   Agent     mils      PCF   FPM                                        ______________________________________                                         1.  CO.sub.2                                                                              0.7    1.9     15.2    17.5  63                                     2.         0.8    1.9     15.0    16.1  70                                     3.         1.0    1.9     14.4    15.0  80                                     4.         1.1    1.9     14.5    13.5  89                                     5.         1.0    1.9     23.0    13.3  57                                     6.         1.0    1.9     32.0    12.3  44                                     7.         1.1    1.9     32.0    11.2  48                                     8.         1.1    1.9     44.0    10.0  40                                     9.         1.3    1.9     60.0    11.0  33                                     ______________________________________                                    

EXAMPLES 1-4

Increasing the amount of carbon dioxide while maintaining relatively constant caliper (@15 mil), results in density decreases from 17.5 to 13.5 PCF. Line speed must be increased to maintain constant caliper.

EXAMPLES 5-9

Slowing the line speed at a given condition will lead to an increase in caliper and a reduction in density. Data shows an increase in carbon dioxide also leads to a density reduction and a line speed increase at a higher (32 mil) caliper level.

The following table summarizes the results of shrinkage of a foam sheet having a thickness of 7 mils and a density of 20 lbs/cu. ft.; at 200° F., 210° F., and 220° F. in the machine direction and cross machine direction.

                  TABLE 11                                                         ______________________________________                                                  200° F.                                                                         210° F.                                                                            220° F.                                                                           Cell                                     Test Sample                                                                               MD     CD     MD   CD    MD   CD   Area                             ______________________________________                                         100% Freon 22                                                                             2.12   -.46   11.91                                                                               -.71  41.31                                                                               4.09 .0173                            W/Skin                                                                         100% Freon 22                                                                             2.98   .28    12.06                                                                               1.33  41.44                                                                               12.21                                                                               .0182                            No/Skin                                                                        CO.sub.2 W/Skin                                                                           2.64   -.02   11.89                                                                               -.01  43.32                                                                               5.56 .0214                            CO.sub.2 No/Skin                                                                          3.68   .10    14.43                                                                               .87   44.53                                                                               12.24                                                                               .0270                            N.sub.2 W/skin                                                                            3.62   -.39   17.73                                                                               1.00  47.23                                                                               6.04 .0277                            N.sub.2 No/Skin                                                                           6.34   -.36   20.90                                                                               1.74  51.00                                                                               11.09                                                                               .0346                            94% N.sub.2 W/Skin                                                                        2.85   -.31   14.76                                                                               .60   46.54                                                                               5.05 .0431                            94% N.sub.2 No/Skin                                                                       3.39   -.07   17.32                                                                               1.57  47.84                                                                               15.39                                                                               .0359                            Comp. Air  2.96   -.14   13.89                                                                               .83   43.78                                                                               5.64 .0336                            W/Skin                                                                         Comp. Air  3.66   .14    16.10                                                                               2.17  44.79                                                                               14.35                                                                               .0314                            No/Skin                                                                        He W/Skin  3.03   .38    17.85                                                                               2.94  47.14                                                                               10.01                                                                               .0384                            ______________________________________                                    

                  TABLE 12                                                         ______________________________________                                         Sheffield Smoothness - Foam/Mandrel Side                                       Blowing Agent                                                                              Unfoamed Layer                                                                             Smoothness  Rating                                     ______________________________________                                         N.sub.2     +           2.17         1-Best                                    N.sub.2     -           2.42         2                                         CO.sub.2    +           3.34         3                                         Air         -           3.92         4                                         Freon 22    +           3.92         4                                         Air         +           4.25         5                                         N.sub.2 (94%)                                                                              +           4.34         6                                         Freon 22    -           4.50         7                                         N.sub.2 (94%)                                                                              -           4.84         8                                         CO.sub.2    -           5.42         9                                         He.sub.2    +           63.80       10-Worst                                   ______________________________________                                          + Yes                                                                          - No                                                                     

It can be seen that the use of atmospheric gases produces varying degrees of smoothness.

Although the invention has been described as preferably applicable to polystyrene foam sheet material, the method is also applicable to utilizing atmospheric gases without, a non-volatile blending agent to make foam polypropylene and polyethylene foam sheet material.

It can thus be seen that there has been provided a method of making polystyrene foam wherein the method utilized atmospheric gases as blowing agents which are inherent in the atmosphere; wherein the blowing agent is substantially entirely released when the polystyrene foam is extruded; wherein the melt can be cooled to normal process levels and not create high loading on the extruder or shear heat from high polymer viscosity; wherein the amount of shrinkage can be controlled as may be required for the ultimate use of the foam; and wherein the density and cell size can be controlled; and which utilizes conventional extrusion apparatus. 

We claim:
 1. An extruded thermoplastic heat shrinkable foam product adapted to be used to form shrinkable labels on containers or cups comprisinga foam thermoplastic material which has been formed by introducing an atmospheric gas into a molten thermoplastic resin containing a blending agent which is substantially non-volatile and has a high molecular weight, continuously extruding said thermoplastic resin through an extruder in the form of a frustoconical tubular web at an angle to the axis of the extruder, continuously pulling and passing said frustoconical web over an internal cooling mandrel to cool the interior of the web, simultaneously applying cooling air to the outside of the frustoconical web, characterized by (a) said product having substantially no residual blowing agent, (b) said product being dimensionally stable at ambient temperature and having substantially no corrugations; (c) said product being sufficiently resilient that it can be compressed to remove gauge bands, (d) said product having shrinkage properties which do not change substantially when the foam material is stored over extended periods of time, (e) said product having a controlled rate of shrinkage at elevated temperatures; (f) said product having cell size, opacity, stiffness, smoothness, caliper, density that do not change over extended time of storage as contrasted to foam thermoplastic material formed using fluorocarbons or hydrocarbon blowing agents.
 2. The product set forth in claim 1 wherein said non-volatile material is of the ester type.
 3. The product set forth in claim 2 wherein said ester is selected from the group consisting of diisodecyl adipate, ditridecyl adipate and trioctyle trimellitate.
 4. The product set forth in claim 3 wherein said non-volatile high molecular weight material has a molecular weight at least
 350. 5. The product set forth in claim 2 wherein said non-volatile material comprises 3% or less by weight of the molten resin.
 6. The product set forth in claim 1 wherein said resin comprises polystyrene. 